Chemical APPLICATION Kinetics viscosity / Temperature on resins

Measuring the changes in resins’ dynamic viscosity over a range of temperatures from 70 to 105°C and comparing them.

    Chemical APPLICATION

    Product

    RM 100 Touch

    Measuring system

    MS-C with disposable aluminium cups

    Software

    VISCO-RM

    Temperature control

    four RT-1

    Shear rate range

    50 s-1

    Temperature

    70-105°C

Method

Set the sample contained in cup C at a temperature of 70°C for 10 minutes in the RT-1 oven;

The measurement consists of increasing the temperature of the RT-1 oven from 70°C to 105°C, and measuring viscosity based on times of 10 minutes, using the VISCO-RM software which leads the RM100 TOUCH viscometer at a shear rate of 50 s-1.

The resulting curve shows changes in kinetics viscosity based on temperature.

Comparing several products by superimposing the curves will show the ability of the products to withstand signifi cant changes in temperature in terms of their viscosity.

Results

Resin A is sensitive to changes in temperature: it is very fl uid at high temperatures >95°C, but becomes very viscous when it cools down, passing from 200 mPa·s at 95°C to 2000 mPa·s at 78°C.
Resin B however, responds completely differently, with a relatively stable viscosity, in this temperature range, of around 700 mPa·s.

Depending on the usage temperature of these resins, their viscosity could be completely inverted:

A is much more viscous than B up to 85°C, and B become more viscous than A upwards of 95°C.

For both resins to be used in a risk-free way, they must be worked with at 90°C.

Do not hesitate to get in touch with us for more information:
Phone: +33 (0)4 78 08 54 06 / contact@lamyrheology.com

Chemical APPLICATION

bottom5

Lamy Rheology is the first French manufacturer of measuring
instruments for laboratories , research and industry.
certification-iso9001
Fleche

gkBottomSection

gkLang